Study on mechanism of extremely low friction of thin carbonaceous films and their applications
| Project/Area Number |
21360076
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (B)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Design engineering/Machine functional elements/Tribology
|
|---|
| Research Institution | Nippon Institute of Technology |
|---|
Principal Investigator |
|
|---|
| Project Period (FY) |
2009 – 2011
|
| Project Status |
Completed (Fiscal Year 2011)
|
| Budget Amount *help |
¥17,030,000 (Direct Cost: ¥13,100,000、Indirect Cost: ¥3,930,000)
Fiscal Year 2011: ¥1,690,000 (Direct Cost: ¥1,300,000、Indirect Cost: ¥390,000)
Fiscal Year 2010: ¥7,020,000 (Direct Cost: ¥5,400,000、Indirect Cost: ¥1,620,000)
Fiscal Year 2009: ¥8,320,000 (Direct Cost: ¥6,400,000、Indirect Cost: ¥1,920,000)
|
|---|
| Keywords | トライボロジー / ダイヤモンドライクカーボン膜 / 境界潤滑 / 積層膜 / 原子間力顕微鏡 / ナノ周期積層膜 / ナノ周期層膜 |
|---|
| Research Abstract |
To realize extremely low friction, nanostructured carbonaceous films such as nanoperiod multilayer films and nanocomposite films were deposited. Evaluation of the structure and composition of the deposited films was performed by surface analysis methods such as transmission electron microscopy and compared with evaluated nanometer-scale mechanical properties. Furthermore, multilayer and nanocomposite films that combined carbon and various metals were deposited, then the relation between the film structure and the boundary lubrication properties was evaluated. Moreover, under boundary lubrication using polyalphaolefin with an additive, carbonaceous nanocomposite films containing Co, Mg or Ti exhibited extremely low friction.
|