Formation of Al2O3 scale on low-Al heat resistant alloys by increasing aluminum outward diffusion flux
Project/Area Number |
21360351
|
Research Category |
Grant-in-Aid for Scientific Research (B)
|
Allocation Type | Single-year Grants |
Section | 一般 |
Research Field |
Material processing/treatments
|
Research Institution | Hokkaido University |
Principal Investigator |
|
Co-Investigator(Kenkyū-buntansha) |
SAKAGUCHI Norihito 北海道大学, 大学院・工学研究院, 准教授 (70344489)
|
Project Period (FY) |
2009 – 2011
|
Project Status |
Completed (Fiscal Year 2011)
|
Budget Amount *help |
¥18,590,000 (Direct Cost: ¥14,300,000、Indirect Cost: ¥4,290,000)
Fiscal Year 2011: ¥2,210,000 (Direct Cost: ¥1,700,000、Indirect Cost: ¥510,000)
Fiscal Year 2010: ¥2,210,000 (Direct Cost: ¥1,700,000、Indirect Cost: ¥510,000)
Fiscal Year 2009: ¥14,170,000 (Direct Cost: ¥10,900,000、Indirect Cost: ¥3,270,000)
|
Keywords | 表面・界面制御 / 高温腐食防食 / 高温酸化 / 耐熱合金・コーティング / アップヒル拡散 / アルミナスケール / 相変態 / 高温酸化防食 / 耐熱合金 / 表面改質 / Ni基合金 / コーティング / Al外方拡散フラックス |
Research Abstract |
Several Ni-low Al alloys with various metal coatings (-100nm) were oxidized at 1150℃ in air. Among the coating elements used in the present study, a thin Pt coating with the optimized heating treatment promoted the formation of Al_2O_3 scale on the Ni-14at%Al alloy. Al uphill outward diffusion was confirmed to occur after the heat treatment, and this Al outward diffusion was considered to cause the formation of Al_2O_3 scale on the Ni-low Al alloys.
|