Research of the polymer-like inorganic-encapsulation film fabricated by the sol-gel method
| Project/Area Number |
21750185
|
|---|
| Research Category |
Grant-in-Aid for Young Scientists (B)
|
| Allocation Type | Single-year Grants |
|---|
| Research Field |
Functional materials/Devices
|
|---|
| Research Institution | Saitama University |
|---|
Principal Investigator |
FUKUDA Takeshi Saitama University, 大学院・理工学研究科, 助教 (40509121)
|
|---|
| Project Period (FY) |
2009 – 2010
|
| Project Status |
Completed (Fiscal Year 2010)
|
| Budget Amount *help |
¥3,510,000 (Direct Cost: ¥2,700,000、Indirect Cost: ¥810,000)
Fiscal Year 2010: ¥1,430,000 (Direct Cost: ¥1,100,000、Indirect Cost: ¥330,000)
Fiscal Year 2009: ¥2,080,000 (Direct Cost: ¥1,600,000、Indirect Cost: ¥480,000)
|
|---|
| Keywords | 有機EL / ゾル-ゲル / 封止 / 酸化チタン / シリカガラス / ゾル-ゲル法 / ガラス / 光劣化特性 / 酸素透過率 |
|---|
| Research Abstract |
Moisture and oxygen cause the degradation of an organic light-emitting diode. Therefore, we investigated the encapsulation technique using one solution process, called as the sol-gel process. We successfully achieved the transparent silica glass thin film with the high-encapsulation performances using phenyltrimethoxysilane and diethoxydimethylsilane in the sol-gel starting solution. In addition, the higher encapsulation performance of the silica glass film was also demonstrated using the solvothermal process.
|