FORMATION MECHANISM OF SPOTANEOUS SUPERLATTICE BY APPLICATION OFMAGNETIC FIELD DURING DEPOSITION AND STRUCTURE INDUCED FERROELECTRICITY
| Project/Area Number |
22360270
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (B)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Inorganic materials/Physical properties
|
|---|
| Research Institution | Shizuoka University |
|---|
Principal Investigator |
WAKIYA Naoki 静岡大学, 工学部, 教授 (40251623)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
SUZUKI Hisao 静岡大学, 創造科学技術大学院, 教授 (70154573)
SAKAMOTO Naonori 静岡大学, 工学部, 助教 (80451996)
|
|---|
| Co-Investigator(Renkei-kenkyūsha) |
SHINOZAKI Kazuo 東京工業大学, 理工学研究科, 教授 (00196388)
FU Desheng 静岡大学, 手グローバル研究リーダー育成拠点, 特認准教授 (30422546)
|
|---|
| Project Period (FY) |
2010 – 2012
|
| Project Status |
Completed (Fiscal Year 2012)
|
| Budget Amount *help |
¥19,110,000 (Direct Cost: ¥14,700,000、Indirect Cost: ¥4,410,000)
Fiscal Year 2012: ¥2,730,000 (Direct Cost: ¥2,100,000、Indirect Cost: ¥630,000)
Fiscal Year 2011: ¥5,330,000 (Direct Cost: ¥4,100,000、Indirect Cost: ¥1,230,000)
Fiscal Year 2010: ¥11,050,000 (Direct Cost: ¥8,500,000、Indirect Cost: ¥2,550,000)
|
|---|
| Keywords | PLD / 磁場印加 / SrTiO3 / 強誘電体 / 超格子 / 強誘電性 / SrTiO_3 |
|---|
| Research Abstract |
Spontaneous formation of superlattice is observed for homoepitaxially grown SrTiO3thin film with Sr-excess composition deposited on Nb-SrTiO3(001) single crystal substrate when the film was deposited using PLD in the magnetic field. It was clarified that this phenomenon is caused by surface-directed spinodal decomposition. This film shows ferroelectricity even at room temperature. This phenomenon would be caused by the internal strain that forms at the interface of layers with different composition.
|