Electric Field Modulation of Giant Thermopower in Oxide Thin FilmTransistors and its Application for IR Sensor
| Project/Area Number |
22360271
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (B)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Inorganic materials/Physical properties
|
|---|
| Research Institution | Hokkaido University (2012)
Nagoya University (2010-2011) |
|---|
Principal Investigator |
OHTA Hiromichi 北海道大学, 電子科学研究所, 教授 (80372530)
|
|---|
| Project Period (FY) |
2010 – 2012
|
| Project Status |
Completed (Fiscal Year 2012)
|
| Budget Amount *help |
¥17,160,000 (Direct Cost: ¥13,200,000、Indirect Cost: ¥3,960,000)
Fiscal Year 2012: ¥4,160,000 (Direct Cost: ¥3,200,000、Indirect Cost: ¥960,000)
Fiscal Year 2011: ¥4,030,000 (Direct Cost: ¥3,100,000、Indirect Cost: ¥930,000)
Fiscal Year 2010: ¥8,970,000 (Direct Cost: ¥6,900,000、Indirect Cost: ¥2,070,000)
|
|---|
| Keywords | 二次元電子ガス / 熱電能 / 電界変調 / 赤外線センサー / 二次元電子ｶﾞｽ |
|---|
| Research Abstract |
Top-gate type thin film transistor structure was fabricated on an oxide semiconductor, SrTiO3 single crystal plate. The electron transport and the thermopower S for the extremely thin two-dimensional electron gas, which can be formed on the SrTiO3 crystal by a gate voltage application, were precisely measured / analyzed. As a result of this study, followings were clarified. 1) Water incorporated nano-porous glass [CAN: H. Ohta et al., Nature Commun. 1: 118 (2010); Adv. Mater. 24, 740 (2012)] is very useful as a gate insulator. 2) Extremely thin 2DEG can be generated on the oxide semiconductor surface when ECBM of the oxide semiconductor is greater than EH2. 3) Extremely thin 2DEG (n3D >4×1021 cm-3) exhibited unusually large S-value, which is five times larger than that of bulk (Figure of merit, ZT~2). This clearly demonstrates that the transistor approach works well as the thermoelectric infrared sensor.
|