Novel composite electrolytes using hetero-interfacial effect and their application to electrochemical devices
| Project/Area Number |
22360336
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (B)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Catalyst/Resource chemical process
|
|---|
| Research Institution | The University of Tokyo |
|---|
Principal Investigator |
KIKUCHI Ryuji 東京大学, 大学院・工学系研究科, 准教授 (40325486)
|
|---|
| Project Period (FY) |
2010 – 2012
|
| Project Status |
Completed (Fiscal Year 2012)
|
| Budget Amount *help |
¥19,630,000 (Direct Cost: ¥15,100,000、Indirect Cost: ¥4,530,000)
Fiscal Year 2012: ¥1,820,000 (Direct Cost: ¥1,400,000、Indirect Cost: ¥420,000)
Fiscal Year 2011: ¥7,930,000 (Direct Cost: ¥6,100,000、Indirect Cost: ¥1,830,000)
Fiscal Year 2010: ¥9,880,000 (Direct Cost: ¥7,600,000、Indirect Cost: ¥2,280,000)
|
|---|
| Keywords | 資源・エネルギー有効利用技術 / 固体電解質 / 無機酸素酸塩 / 界面伝導相 / 燃料 電池 / エネルギー効率化 / 燃料電池 / 有効媒質近似 / ピロリン酸シリカ / リン酸二水素セシウム |
|---|
| Research Abstract |
Novel composite electrolytes based on phosphate and oxide matrix were investigated for intermediate fuel cells operative at 200-300°C, and the promotional effect of the hetero-interface between the conductive phase and matrix was examined. Interfacial conductive phase was formed between phosphate and SiO2 treated with phosphoric acid, leading to an increase in the conductivity. CsH5(PO4)2/SiO2 composite membrane employing silica fiber membrane as a matrix with a thickness of 70 and 150 μm was fabricated and applied to an electrolyte for an intermediate-temperature fuel cell, which demonstrated good performance of 105 mW cm-2 at 200°C due to a low area specific resistance of 0.32 Ω cm2, and was stable at 200°C under a constant current load of 100 mA cm-2 for 50 h.
|