Improvement of rolling contact fatigue strength of ceramics by self-crack healing
| Project/Area Number |
22686013
|
|---|
| Research Category |
Grant-in-Aid for Young Scientists (A)
|
| Allocation Type | Single-year Grants |
|---|
| Research Field |
Materials/Mechanics of materials
|
|---|
| Research Institution | Yokohama National University |
|---|
Principal Investigator |
TAKAHASHI Koji 横浜国立大学, 大学院・工学研究院, 教授 (90334630)
|
|---|
| Project Period (FY) |
2010 – 2012
|
| Project Status |
Completed (Fiscal Year 2012)
|
| Budget Amount *help |
¥17,550,000 (Direct Cost: ¥13,500,000、Indirect Cost: ¥4,050,000)
Fiscal Year 2012: ¥2,210,000 (Direct Cost: ¥1,700,000、Indirect Cost: ¥510,000)
Fiscal Year 2011: ¥2,730,000 (Direct Cost: ¥2,100,000、Indirect Cost: ¥630,000)
Fiscal Year 2010: ¥12,610,000 (Direct Cost: ¥9,700,000、Indirect Cost: ¥2,910,000)
|
|---|
| Keywords | セラミックス / 転動疲労強度 / 自己き裂治癒 / ショットピーニング / 残留応力 / 破壊靱性値 / 圧縮残留応力 / 自己き裂治ゆ / 破壊靭値性 |
|---|
| Research Abstract |
Ceramics are expected as high performance bearings. So investigation of the rolling contact fatigue strength is crucially important. To evaluate the effects of the shot peening and crack-healing on the rolling contact fatigue strength, rolling contact fatigue tests were carried out on Si3N4 and Al2O3/SiC composite. For Si3N4 ceramics, the rolling contact fatigue strength was improved by shot peening. For Al2O3/SiC composite the rolling contact fatigue strength increased by combination of shot peening and crack-healing.
|