| Project/Area Number |
22750188
|
|---|
| Research Category |
Grant-in-Aid for Young Scientists (B)
|
| Allocation Type | Single-year Grants |
|---|
| Research Field |
Inorganic industrial materials
|
|---|
| Research Institution | Kyoto University |
|---|
Principal Investigator |
FUJITA Koji 京都大学, 大学院・工学研究科, 准教授 (50314240)
|
|---|
| Project Period (FY) |
2010 – 2011
|
| Project Status |
Completed (Fiscal Year 2011)
|
| Budget Amount *help |
¥4,030,000 (Direct Cost: ¥3,100,000、Indirect Cost: ¥930,000)
Fiscal Year 2011: ¥1,300,000 (Direct Cost: ¥1,000,000、Indirect Cost: ¥300,000)
Fiscal Year 2010: ¥2,730,000 (Direct Cost: ¥2,100,000、Indirect Cost: ¥630,000)
|
|---|
| Keywords | 金属酸化物 / 多孔体 / ナノ粒子 / 波動干渉 / 光機能 / 金属ナノ粒子 / 電磁波干渉 / ランダムレーザー / 光機能性材料 / 光貯蔵 |
|---|
| Research Abstract |
Porous oxide materials with controlled morphology have been fabricated using the sol-gel method accompanied by phase separation in order to examine the transport properties of photon. When high-refractive-index TiO_2 porous materials are combined with solution containing organic dye, random laser oscillation is observed as a result of the photon localization. The research on Ce^<3+>: YAG porous materials revealed that some surface defects induce the photoreaction of Ce^<3>+, which results in a novel optical function exemplified by a scattering-based hole burning effect. As the related phenomenon, it is also found that the combination of metal-dielectric core-shell nanoparticles and organic dye solution serves as the random lasing media with low threshold.
|