| Project/Area Number |
22760511
|
|---|
| Research Category |
Grant-in-Aid for Young Scientists (B)
|
| Allocation Type | Single-year Grants |
|---|
| Research Field |
Inorganic materials/Physical properties
|
|---|
| Research Institution | Nagaoka University of Technology |
|---|
Principal Investigator |
HONMA Tsuyoshi 長岡技術科学大学, 工学部, 助教 (70447647)
|
|---|
| Project Period (FY) |
2010 – 2011
|
| Project Status |
Completed (Fiscal Year 2011)
|
| Budget Amount *help |
¥4,160,000 (Direct Cost: ¥3,200,000、Indirect Cost: ¥960,000)
Fiscal Year 2011: ¥1,170,000 (Direct Cost: ¥900,000、Indirect Cost: ¥270,000)
Fiscal Year 2010: ¥2,990,000 (Direct Cost: ¥2,300,000、Indirect Cost: ¥690,000)
|
|---|
| Keywords | 機能性ガラス / 結晶化ガラス / レーザー誘起結晶化 / ゾルーゲル法 / ゾルゲル法 / レーザー照射 / 結晶化 / 非線形光学 / ガラス / レーザー結晶化 / ゾルゲル |
|---|
| Research Abstract |
In this study we examined the fabrication of laser-induced crystallized patterns, in which consisted from LiNbO_3 and Gd_2(MoO_4)_3 from sol-gel derived Li_2O-Nb_2O_5-SiO_2 and Gd_2O_3-MoO_3 amorphous film. Transparent and crack-free amorphous gel films were obtained from both Li_2O-Nb_2O_5-SiO_2 and GdO_2O_3-MoO_3 precursor solution. Furthermore laser-induced crystallization of LiNbO_3 and Gd_2(MoO_4)_3 was successfully performed on the amorphous thin film surface.
|