Development of novel ultralight and superstrong hybrid materials made of low density metals/alloys reinforced with boron nitride nanotubes for automobile and aerospace applications
| Project/Area Number |
23310082
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (B)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Nanomaterials/Nanobioscience
|
|---|
| Research Institution | National Institute for Materials Science |
|---|
Principal Investigator |
GOLBERG Dmitri 独立行政法人物質・材料研究機構, 国際ナノアｰキテクトニクス研究拠点, ユニット長 (80354405)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
BANDO Yoshio (独)物質・材料研究機構, 国際ナノアーキテクトニクス研究拠点, 最高運営責任者 (10344433)
ZHI ChunYi (ZHI Chunyi) 独立行政法人物質・材料研究機構, その他部局等, 研究員 (50469764)
|
|---|
| Project Period (FY) |
2011-04-01 – 2014-03-31
|
| Project Status |
Completed (Fiscal Year 2013)
|
| Budget Amount *help |
¥12,480,000 (Direct Cost: ¥9,600,000、Indirect Cost: ¥2,880,000)
Fiscal Year 2013: ¥2,470,000 (Direct Cost: ¥1,900,000、Indirect Cost: ¥570,000)
Fiscal Year 2012: ¥2,340,000 (Direct Cost: ¥1,800,000、Indirect Cost: ¥540,000)
Fiscal Year 2011: ¥7,670,000 (Direct Cost: ¥5,900,000、Indirect Cost: ¥1,770,000)
|
|---|
| Keywords | 複合材料 / 低密度金属 / 電子顕微鏡 / ナノチューブ / 機能的機能 / 機械的機能 |
|---|
| Research Abstract |
Aluminum/Boron nitride nanotube (BNNT) composites with up to 5 wt% (i.e. 9.7 vol%) nanotube fractions were prepared via various powder metallurgy routes, namely, Spark Plasma Sintering (SPS) and High Pressure Torsion (HPT) methods. Optical microscopy, transmission electron microscopy, scanning electron microscopy, X-ray diffraction, and energy dispersive X-ray analysis confirmed the integration of the two phases into decently dense and compact composites. No other phases, like Al borides or nitrides, form in the Al-BNNTs macrocomposites of the two series. The hardness of HPT samples was drastically increased with increasing BNNTs content in Al pellets. The value for Al-BNNT 3.0 wt% sample was more than doubled (190 MPa) compared to a pure Al HPT compact (90 MPa). And the room temperature ultimate tensile strength of Al-BNNTs HPT samples containing 3.0 wt% BNNT (~300 MPa) became ~1.5 times larger than that of a BNNT-free HPT Al compact (~200 MPa).
|
Report
(4 results)
Research Products
(39 results)
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
[Presentation] Al/BN nanotube composites2013
Author(s)
Maho Yamaguchi, Fanqiang Meng, Konstantin Faerstein, Yoshio Bando, Koichi Tsuchiya, Dmitri Golberg
Organizer
Nanotube 2013
Place of Presentation
Espoo,Finland
Related Report
-
-
-
-
-
-
-
-
-
-
-
-
-