Preparation of uniform contact-interface applying nanocrystalline silicide with controlled crystalline grain size
| Project/Area Number |
23560353
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Multi-year Fund |
|---|
| Section | 一般 |
|---|
| Research Field |
Electronic materials/Electric materials
|
|---|
| Research Institution | Kitami Institute of Technology |
|---|
Principal Investigator |
NOYA Atsushi 北見工業大学, 工学部, 教授 (60133807)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
TAKEYAMA Mayumi B 北見工業大学, 工学部, 准教授 (80236512)
|
|---|
| Project Period (FY) |
2011 – 2013
|
| Project Status |
Completed (Fiscal Year 2013)
|
| Budget Amount *help |
¥5,460,000 (Direct Cost: ¥4,200,000、Indirect Cost: ¥1,260,000)
Fiscal Year 2013: ¥1,040,000 (Direct Cost: ¥800,000、Indirect Cost: ¥240,000)
Fiscal Year 2012: ¥1,560,000 (Direct Cost: ¥1,200,000、Indirect Cost: ¥360,000)
Fiscal Year 2011: ¥2,860,000 (Direct Cost: ¥2,200,000、Indirect Cost: ¥660,000)
|
|---|
| Keywords | 電気・電子材料 / シリサイド / NiSi / NiSi2 / 低温形成 / Niシリサイド / Ni結晶粒 / 界面平坦性 / 結晶粒成長 |
|---|
| Research Abstract |
We have examined the formation of a uniform NiSi/Si contact-interface by reducing its crystalline grain size under the appropriate preparation conditions. It is revealed that the temperature during Ni sputter-deposition on the heated Si substrate and that during the following annealing process are important to reduce the crystalline grain size. Under a certain temperature, the growth of NiSi2, a high temperature phase, occurs at a lower temperature, resulting in the degradation of the uniform interface. It is speculated that the low temperature formation of NiSi2 is owing to the formation of an interdiffused Ni-Si layer with a concentration gradient of Ni, in which NiSi2 will nucleate from an alloy region in a Si-rich composition. We confirm the NiSi2 formation in the system of Ni on SiO2/Si, in which the Ni diffusion through a thin SiO2 layer reduces the diffusivity of Ni species, resulting in the formation of a Si-rich Ni-Si alloy from which NiSi2 will nucleate.
|
Report
(4 results)
Research Products
(9 results)