Colloidal Crystallization and Glass Transition of Polymer Microgels
Project/Area Number |
24550248
|
Research Category |
Grant-in-Aid for Scientific Research (C)
|
Allocation Type | Multi-year Fund |
Section | 一般 |
Research Field |
Polymer/Textile materials
|
Research Institution | The University of Shiga Prefecture (2014) Nagaoka University of Technology (2012-2013) |
Principal Investigator |
|
Project Period (FY) |
2012-04-01 – 2015-03-31
|
Project Status |
Completed (Fiscal Year 2014)
|
Budget Amount *help |
¥5,460,000 (Direct Cost: ¥4,200,000、Indirect Cost: ¥1,260,000)
Fiscal Year 2014: ¥1,300,000 (Direct Cost: ¥1,000,000、Indirect Cost: ¥300,000)
Fiscal Year 2013: ¥1,950,000 (Direct Cost: ¥1,500,000、Indirect Cost: ¥450,000)
Fiscal Year 2012: ¥2,210,000 (Direct Cost: ¥1,700,000、Indirect Cost: ¥510,000)
|
Keywords | マイクロゲル / コロイド結晶 / コロイドガラス / フォトニック結晶 / 結晶化 / ガラス化 / ゲル / 高分子ゲル / 光散乱 / 高分子マイクロゲル |
Outline of Final Research Achievements |
Colloidal crystallization dynamics of poly(N-isopropylacrylamide) microgel was investigated by using optical microscopy (OM), UV-Vis spectroscopy and so on. Nucleation rate and crystal growth rate of the colloidal crystal were estimated from the OM observation. It was found that giant single crystal of the colloidal crystal is obtained near the melting temperature. Crystal growth rate was analyzed based on well-known Wilson-Frenkel law. The growth rate can be well described by the equation on the assumption that colloidal particles have no enthalpic interaction with each other.
|