Development of noble metal nanoparticle-modified base metal wire electrodes with exploring their functions for electroanalysis

Research Project

Project/Area Number	24K08462
Research Category	Grant-in-Aid for Scientific Research (C)
Allocation Type	Multi-year Fund
Section	一般
Review Section	Basic Section 34020:Analytical chemistry-related
Research Institution	Kyoto University
Principal Investigator	小山宗孝京都大学, 工学研究科, 准教授 (90221861)
Project Period (FY)	2024-04-01 – 2027-03-31
Project Status	Granted (Fiscal Year 2024)
Budget Amount *help	¥4,420,000 (Direct Cost: ¥3,400,000、Indirect Cost: ¥1,020,000) Fiscal Year 2026: ¥1,430,000 (Direct Cost: ¥1,100,000、Indirect Cost: ¥330,000) Fiscal Year 2025: ¥1,560,000 (Direct Cost: ¥1,200,000、Indirect Cost: ¥360,000) Fiscal Year 2024: ¥1,430,000 (Direct Cost: ¥1,100,000、Indirect Cost: ¥330,000)
Keywords	貴金属ナノ粒子 / 修飾電極 / ボルタンメトリー / 電気化学分析 / ガルバニ置換反応
Outline of Research at the Start	卑金属線を貴金属イオン水溶液に浸漬すると、酸化還元反応が自発的に進行し、卑金属線表面に貴金属ナノ粒子を簡便に析出・修飾できる。この方法で作製した貴金属ナノ粒子修飾卑金属線電極は、電気分析用電極としてみた場合、常識的には卑金属線の特性として、測定できる電位範囲が限定される。しかし、適切な前電解などを行えば、卑金属表面を電気化学的に不活性化して、貴金属ナノ粒子が電子移動部位として機能するユニークな電気分析用電極を構築できる。本研究では、貴金属ナノ粒子修飾卑金属線電極を作製して、電気化学分析における実用性を探る。