Creation of tough acrylic films with orientation network structure formed by photoplasticization and hot-stretching

Research Project

Project/Area Number	24K08525
Research Category	Grant-in-Aid for Scientific Research (C)
Allocation Type	Multi-year Fund
Section	一般
Review Section	Basic Section 35020:Polymer materials-related
Research Institution	Nagoya Institute of Technology
Principal Investigator	信川省吾名古屋工業大学, 工学(系)研究科(研究院), 准教授 (50609211)
Project Period (FY)	2024-04-01 – 2027-03-31
Project Status	Granted (Fiscal Year 2024)
Budget Amount *help	¥4,550,000 (Direct Cost: ¥3,500,000、Indirect Cost: ¥1,050,000) Fiscal Year 2026: ¥1,170,000 (Direct Cost: ¥900,000、Indirect Cost: ¥270,000) Fiscal Year 2025: ¥1,170,000 (Direct Cost: ¥900,000、Indirect Cost: ¥270,000) Fiscal Year 2024: ¥2,210,000 (Direct Cost: ¥1,700,000、Indirect Cost: ¥510,000)
Keywords	光可塑化 / 配向網目構造 / アクリルフィルム / 強靭化 / アゾベンゼン
Outline of Research at the Start	アクリルガラスとして知られるポリメタクリル酸メチル（PMMA）は、透明性、力学強度に優れるが、10%以下のひずみで破壊する（脆性）という欠点がある。一方、加熱延伸等で分子鎖を配向させると強靭化することが知られているが、力学的な異方性を伴うため、材料全体の強靭化は難しい。そこで本研究では、我々が過去に見出した光可塑化技術と加熱延伸と組み合わせることで配向網目構造をPMMAフィルム中に形成し、強靭化（弾性率＞3 GPa、破断ひずみ＞100%）させることを目指す。