Covalency and metallicity in dissimilar metal nanosheet reactants for alloying

• Project/Area Number: 24K08564
• Research Category: Grant-in-Aid for Scientific Research (C)
• Allocation Type: Multi-year Fund
• Section: 一般
• Review Section: Basic Section 36010:Inorganic compounds and inorganic materials chemistry-related
• Research Institution: Kyoto University
• Principal Investigator: 福田 勝利 京都大学, 成長戦略本部, 教授 (80504331)
• Project Period (FY): 2024-04-01 – 2027-03-31
• Project Status: Granted (Fiscal Year 2024)
• Budget Amount: ¥4,680,000 (Direct Cost: ¥3,600,000、Indirect Cost: ¥1,080,000); Fiscal Year 2026: ¥910,000 (Direct Cost: ¥700,000、Indirect Cost: ¥210,000); Fiscal Year 2025: ¥1,040,000 (Direct Cost: ¥800,000、Indirect Cost: ¥240,000); Fiscal Year 2024: ¥2,730,000 (Direct Cost: ¥2,100,000、Indirect Cost: ¥630,000)
• Keywords: Nanosheets / Topotactic conversion / Alloy / Dissimilar Metal

Outline of Research at the Start

「二次元ナノ金属」は、数あるナノ金属の中でも大きな構造異方性を有することから、三次元バルクの状態と比べて、それらの構成元素は必然的に特異な結合状態を形成している。構成元素間の結合状態と金属状態の発現は密接に結びついており、原子層数を厳密に制御した二次元ナノ金属反応炉の設計は、金属の新たな側面の理解につながる。本研究では、我々が合成してきたルテニウムおよび白金ナノシートをモデル金属ナノシートとして、積層数、順番、比率を変えた異種金属ナノシート反応炉を構築する。そして、どの組成、構造で分子性を維持するのか？合金を形成するのか？を調べることで、二次元ナノ金属の物性発現のメカニズムを探求する。