Syntheses and applications of low-dimensional nanostructured ceramics thin film/metal composites
| Project/Area Number |
25420732
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Multi-year Fund |
|---|
| Section | 一般 |
|---|
| Research Field |
Composite materials/Surface and interface engineering
|
|---|
| Research Institution | Saga University |
|---|
Principal Investigator |
Mitsunori Yada 佐賀大学, 工学(系)研究科(研究院), 准教授 (20274772)
|
|---|
| Co-Investigator(Renkei-kenkyūsha) |
NOGUCHI Hideyuki 佐賀大学, 大学院工学系研究科, 教授 (60093978)
|
|---|
| Project Period (FY) |
2013-04-01 – 2016-03-31
|
| Project Status |
Completed (Fiscal Year 2015)
|
| Budget Amount *help |
¥5,200,000 (Direct Cost: ¥4,000,000、Indirect Cost: ¥1,200,000)
Fiscal Year 2015: ¥520,000 (Direct Cost: ¥400,000、Indirect Cost: ¥120,000)
Fiscal Year 2014: ¥520,000 (Direct Cost: ¥400,000、Indirect Cost: ¥120,000)
Fiscal Year 2013: ¥4,160,000 (Direct Cost: ¥3,200,000、Indirect Cost: ¥960,000)
|
|---|
| Keywords | リン酸チタン / 酸化チタン / リチウムイオン電池 / ナトリウムイオン電池 / 濡れ性 / イオン交換 / 薄膜 / Ｌｉイオン電池 / 超撥水 / ナノ構造 / 光触媒 |
|---|
| Outline of Final Research Achievements |
The hydrothermal reaction of a titanium plate in a mixed aqueous solution of hydrogen peroxide and phosphoric acid under different conditions resulted in the formation of titanium phosphate particles and thin films with various crystal structures and morphologies. Wettability of the titanium phosphate thin films, including superhydrophilicity, superhydrophobicity, and adhesion force between a water droplet and the thin films, could be controlled. A silver nanoparticle/silver titanium phosphate nanobelt thin film showed excellent antibacterial activity against MRSA. The titanium phosphate particles and thin films could be transformed into hierarchical porous TiO2 particles and thin films while keeping their morphologies. The hierarchical porous TiO2 particles showed excellent characteristics of lithium-ion and sodium-ion batteries and removal of organic molecules in aqueous solutions by adsorption and photocatalytic degradation.
|