Preparation of Ordered Porous Alumina Through-Hole Membrane by Two-Layer Anodization
| Project/Area Number |
26390021
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Multi-year Fund |
|---|
| Section | 一般 |
|---|
| Research Field |
Nanomaterials chemistry
|
|---|
| Research Institution | Tokyo Metropolitan University |
|---|
Principal Investigator |
|
|---|
| Project Period (FY) |
2014-04-01 – 2017-03-31
|
| Project Status |
Completed (Fiscal Year 2016)
|
| Budget Amount *help |
¥4,940,000 (Direct Cost: ¥3,800,000、Indirect Cost: ¥1,140,000)
Fiscal Year 2016: ¥1,170,000 (Direct Cost: ¥900,000、Indirect Cost: ¥270,000)
Fiscal Year 2015: ¥1,950,000 (Direct Cost: ¥1,500,000、Indirect Cost: ¥450,000)
Fiscal Year 2014: ¥1,820,000 (Direct Cost: ¥1,400,000、Indirect Cost: ¥420,000)
|
|---|
| Keywords | 陽極酸化 / ポーラスアルミナ / スルーホールメンブレン / 陽極酸化ポーラスアルミナ |
|---|
| Outline of Final Research Achievements |
Ordered anodic porous alumina through-hole membranes were prepared by two-layer anodization using concentrated sulfuric acid solution. Hole period in anodic porous alumina through-hole membrane could be controlled by adjusting anodization voltage. Ideally ordered porous alumina through-hole membranes could also be obtained by a combination of the pretexturing of Al and subsequent two-layer anodization. The obtained ordered through-hole membranes are expected to be used in various functional application fields.
|