異種金属上に形成した貴金属超薄層触媒の構築過程の追跡とその３Ｄ活性サイトの探索
Publicly Offered Research
| Project Area | 3D Active-Site Science |
|---|
| Project/Area Number |
15H01045
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research on Innovative Areas (Research in a proposed research area)
|
| Allocation Type | Single-year Grants |
|---|
| Review Section |
Science and Engineering
|
|---|
| Research Institution | Ochanomizu University |
|---|
Principal Investigator |
近藤 敏啓 お茶の水女子大学, 基幹研究院, 教授 (70240629)
|
|---|
| Project Period (FY) |
2015-04-01 – 2017-03-31
|
| Project Status |
Completed (Fiscal Year 2016)
|
| Budget Amount *help |
¥6,630,000 (Direct Cost: ¥5,100,000、Indirect Cost: ¥1,530,000)
Fiscal Year 2016: ¥3,380,000 (Direct Cost: ¥2,600,000、Indirect Cost: ¥780,000)
Fiscal Year 2015: ¥3,250,000 (Direct Cost: ¥2,500,000、Indirect Cost: ¥750,000)
|
|---|
| Keywords | 単結晶電極 / 異種金属析出 / 表面X線散乱法 / 電極触媒 / ３Ｄ活性点 / 表面Ｘ線散乱法 |
|---|
| Outline of Annual Research Achievements |
Au(111)単結晶上に自己終端化析出法で形成させた白金超薄膜は、下地構造を反映したpseudomorphic構造をとっていることを明らかとした。
その他、今年度の成果として、1) カーボネート系溶媒中において、Si(111)上に形成させたLixSiy合金相は、三角錐状の形状をしたLi15Si4単結晶相、Li15Si4またはLi13Si4合金のアモルファス相、及びSi単結晶相とLi15/13Si4合金のアモルファス相との混合相から成る３層構造であったのに対し、Si(100)上に形成させたそれでは、四角錐状の形状をしたLi15Si4単結晶相、Li15Si4またはLi13Si4合金のアモルファス相、及びSi単結晶相中にLi金属が入り込んだ混合相から成る３層構造であることを証明、2) Si(111)単結晶上に構築したビオロゲン自己組織化単分子層に種々の貴金属イオンを吸着させて作成した貴金属触媒層の水素発生及び二酸化炭素還元能について、構造と触媒能との定量的関係を解明、3) Au(111)単結晶上に、金属イオンと有機配位子から成る３次元有機金属錯体の構造制御した状態で１層ずつ積層して行くことに成功、4) 卑金属で安価なニッケルをコアに、貴金属で触媒活性が高い白金をシェルにもつ、コアシェル型微粒子触媒を電気化学的に構築することに成功し、非常に高い酸素還元触媒活性を達成、があげられる。
|