| キーワード | Co-Ni-based superalloy / gamma prime / Suzuki segregation / creep resistance |
|---|
| 研究実績の概要 |
The microstructure of the designed Co-Ni-based superalloy which is strengthened by gamma prime phase and Suzuki segregation was observed using in-situ TEM at high temperature of 700 centigrade. The in-situ TEM observation is a powerful method to figure out how the stacking fault form and broaden due to the segregation of solute atoms (Suzuki segregation) via recording the movement of dislocation.
Beside that several button shaped alloys with the addition of Re and/or B were prepared using arc melting method. The hot forging was carried out at 1200 centigrade to obtain the homogeneous microstructure. With addition of Re and/or B, precipitate can form along grain boundary to enhance the grain boundary strength. Thus the creep resistance is expected to be enhanced.
|
| 現在までの達成度 (区分) |
現在までの達成度 (区分)
2: おおむね順調に進展している
理由
Several button-shaped alloys have been prepared using arc melting method with addition of 3% Re while 0-0.1 B. The hot forging has been carried out at 1200 centigrade to obtain the homogeneous microstructure. The microstructure has been observed after hot forging. Beside that, in-situ TEM observation has been performed sevaral times at 700 centigrade to try to observe the motion of dislocation.
|
| 今後の研究の推進方策 |
1. The in-situ TEM observation will be conducted using STEM in future because the normal TEM has low magnification and the oxidation occurred during heating.
2. The cold rolling and aging at various temperatures will be performed in next step.
3. The microstructure in particular along the grain boundary will be observed to check the precipitate along grain boundary.
4.The tensile tests and the stress relaxation tests at high temperatures will be carried out to examine the creep resistance.
|