2004 Fiscal Year Final Research Report Summary
The study on enhancement effect of photocatalytsis under visible light irradiation with the oxide photocatalysts
| Project/Area Number |
14350341
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (B)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Physical properties of metals
|
|---|
| Research Institution | Niigata University (2003-2004)
Shimane University (2002) |
|---|
Principal Investigator |
YAMADA Yuh Niigata University, Faculty of Science, Professor, 理学部, 教授 (10242835)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
KUBO Syugo Shimane University, Interdisciplinary Faculty of Science and Engineering, Professor, 総合理工学部, 教授 (30294359)
MATSUSHITA Akiyuki Materials Engineering Laboratory, NIMS, Associate Professor, 材料研究所・基礎物性グループ, アソシエイトディレクター(研究職) (30343859)
YE Jinhua Ecomaterials Center, NIMS, Senior Researcher, エコマテリアル研究センター, 主幹研究員 (90230630)
GOTO Terutaka Niigata University, Graduate School of Science and Technology, Professor, 大学院・自然科学研究科, 教授 (60134053)
NEMOTO Yuichi Niigata University, Graduate School of Science and Technology, Associate Professor, 大学院・自然科学研究科, 助教授 (10303174)
|
|---|
| Project Period (FY) |
2002 – 2004
|
| Keywords | Photocatalysts / Oxide / The crystal structural / Electric properties / Visible light irradiation / The effects of pressure |
|---|
| Research Abstract |
Since photo-induced decomposition of water on TiO_2 electrodes was discovered, semiconductor-based photocatalysis has attracted extensive interest. Most of the investigations have focused on TiO_2, which shows relatively high activity and chemical stability under UV light irradiation. Therefore, there is an urgent need to develop new types of photocatalysts that can yield high activity under visible light irradiation, because the attempt is aimed at producing hydrogen of clean-energy from water utilizing solar energy. We have investigated the electric and crystal structural changes on the oxide photocatalysts, resulting in a change in photocatalytLc property. The results are explained in the following.
1.In addition to the reported InTaO_4 and InNbO_4 photocatalysts, 3d transition metal V compound InVO_4 was found to be a visible light driven photocatalyst for H_2 evolution from pure water. Then, we have also investigated the substitute system MVO_4 under high pressure. We found the phase transition in CeVO_4 up to 6 GPa.
2.We have demonstrated efficiently photocatalytic degradation of methylene blue dye over the oxide photocatalyst R_2BaCuO_5(R=lanthanoid) under visible light irradiation. Nd_2BaCuO_5 oxide was found the high activity under visible light irradiation.
3.We have found superconductivity in the Pr_2Ba_4Cu_7O_<15-δ> possessing metallic double chains when the oxide photocatalysts were searched.
|
Research Products
(42 results)
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
[Journal Article] High-resolution photoelectron spectroscopy of Heusler-type Fe_2VAl alloy2002
Author(s)
K.Soda, T.Mizutani, O.Yoshimoto, S.Yagi, U.Mizutani, H.Sumi, Y.Nishino, Y.Yamada, T.Yokoya, S.Shin, A.Sekiyama, S.Suga
-
Journal Title
J.Synchrotron Radiation Volume 9
Pages: 233-236
Description
「研究成果報告書概要(欧文)」より
-
-