2004 Fiscal Year Final Research Report Summary
Cutting performance of edge-sharpened thick diamond-film brazed milling tools
| Project/Area Number |
15580148
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
林産科学・木質工学
|
|---|
| Research Institution | HIROSHIMA UNIVERSITY |
|---|
Principal Investigator |
BANSHOYA Kaoru Hiroshima University, Graduate School of Education, Professor, 大学院・教育学研究科, 教授 (50101449)
|
|---|
| Project Period (FY) |
2003 – 2004
|
| Keywords | wood machining / wood cutting tool / diamond-film brazed tool / tool-life |
|---|
| Research Abstract |
Sharpening cutting-edge of thick diamond-film brazed tool to make wood cutting tool with sharp cutting-edge and long tool-life was taken note of in this study. The diamond-film brazed tool was made, it was confirmed that cutting-edge roundness of the tool became small and its surface became flat as compared with the diamond-coated tool. Cutting tests for the edge-sharpened thick diamond-film brazed tool, diamond-coated tool and uncoated tool in the milling of thirteen kinds of woods and three kinds of wood-based materials with a spindle shaper were performed, the difference in cutting power consumption by tool for each work material was examined and the value for cutting-edge of thick diamond-film brazed tool was compared with those for other tools. Furthermore tool-life tests for three tools in the milling of melapi or MDF were performed, the difference in tool-wear progression by tool was examined. From the results of cutting test, cutting performance of the edge-sharpened thick diamond-film brazed milling tool was examined and the superiority as the milling tool was clarified from the view point of long tool-life.
|