2017 Fiscal Year Final Research Report
3D Conductive Area of Solution-Processed ZnO Layer and Transparent Flexible LED
| Project/Area Number |
15H04122
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (B)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Inorganic materials/Physical properties
|
|---|
| Research Institution | Tokyo Institute of Technology |
|---|
Principal Investigator |
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
我田 元 明治大学, 理工学部, 専任講師 (40633722)
|
|---|
| Research Collaborator |
Hong Jeongsoo
|
|---|
| Project Period (FY) |
2015-04-01 – 2018-03-31
|
| Keywords | 酸化亜鉛薄膜 / 透明導電性 / 溶液作製 |
|---|
| Outline of Final Research Achievements |
Solution-processed ZnO films could exhibit transparent conductivity after UV irradiation. The irradiation of UV-A and UV(λ = 380 nm) only for 1 hour attained the conductivity. The transparent circuit was drawn by UV laser irradiation and the conductive are had 3 order lower resistivity than without irradiation area. The rectification property was obtained the ZnO films deposited on p-Si and p-GaN substrate. The Mn doped ZnO film exhibited the saturation magnetization of 1.68x10-2 emu/g.
It is valuable result that the transparent conductive magnetic ZnO film could be fabricated by solution process.
|
| Free Research Field |
無機材料
|