2005 Fiscal Year Final Research Report Summary
FUNDAMENTAL STUDIES ON RADICAL POLYMERIZATION OF RODLIKE MACROMONOMERS
| Project/Area Number |
16550105
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Polymer chemistry
|
|---|
| Research Institution | Yamagata University |
|---|
Principal Investigator |
KAWAGUCHI Seigo Yamagata University, Faculty of Engineering, Professor, 工学部, 教授 (00204694)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
NAGAI Katsutoshi Yamagata University, Faculty of Engineering, Professor, 工学部, 教授 (00005498)
|
|---|
| Project Period (FY) |
2004 – 2005
|
| Keywords | RODLIKE POLYMER / MACROMONOMER / GRAFT POLYMER / REACTIVITY RATIO / LIVING RADICAL POLYMERIZATION / LIGHT SCATTERING / HELICAL POLYMER / SOLUTION PROPERTIES |
|---|
| Research Abstract |
Styryl- and methacrylate-ended rodlike macromonomers consisting of poly(n-hexyl isocyanate) (VB-HIC-n and MA-HIC-n) with relatively narrow molecular weight distribution (Mw/Mn < 1.2) have successfully been prepared in CH_2Cl_2 at room temperature by living coordination polymerization of n-hexyl isocyanate (HIC) using 4-vinylbenzyloxy- and 2-methacrylate ethyloxy-dichloro(cyclopentadienyl)titanium(IV) as initiator, respectively. The radical copolymerization behavior of the rodlike macromonomers with corresponding low molecular weight monomers such as styrene or MMA has been studied and summarized as a function of degree of polymerization of HIC. In the copolymerization of VB-HIC-n with styrene, the apparent copolymerizabilities of the rodlike macromonomer (1/r_1) seem to be almost equivalent to the styrene, suggesting that the reactivity is mainly determined by the chemical reactivity of the ended double bond. On the other hand, in the copolymerization of MA-HIC-n macromonomers with MMA the value of 1/r_1 is almost constant for total monomer concentration and degree of polymerization but lower than that of MMA, most likely due to the incompativility between MA-HIC-n and PMMA propagating chain.
Radical homopolymerization of the macromonomers affords novel well-defined comblike, cylindrical brushes consisting of the rods as a branched chain. The dimensional properties of the brushes have been studied by means of light scattering, SAXS, and viscometry. The molecular weight dependence of radius of gyration of the brushes in dilute solution is analyzed in terms of wormlike chain model and rationalized as a function of the side chain length of the rods. The Kuhn statistical length of the brushes is found to linearly increase with the rod length.
|