2017 Fiscal Year Final Research Report
Synthesis of perovskite oxide thin films showing rattling behavior and their application to thermoelectric conversion materials
| Project/Area Number |
16K14092
|
|---|
| Research Category |
Grant-in-Aid for Challenging Exploratory Research
|
| Allocation Type | Multi-year Fund |
|---|
| Research Field |
Inorganic industrial materials
|
|---|
| Research Institution | Kyoto University |
|---|
Principal Investigator |
|
|---|
| Project Period (FY) |
2016-04-01 – 2018-03-31
|
| Keywords | 酸化物 / ペロブスカイト型構造 / 高圧合成 / 構造解析 / 熱分解 / 熱分析 / トポケミカル反応 / 反応エンタルピー |
|---|
| Outline of Final Research Achievements |
By utilizing the solid-state reaction at elevated temperature and pressure, we succeeded in synthesizing new metastable oxides, CuNbO3 and CuTaO3, which possess the perovskite structure. The second-harmonic generation measurements reveal that those compounds have a polar structure. It was found that the resultant compounds undergo thermal decomposition reaction to form both CuO and A-site ordered quadruple perovskite oxides with some of the A-sites having cation vacancies. The reaction enthalpy was evaluated by using the thermal analysis. We also examined the thermal decomposition of CuNbO3 obtained by the solid-state reaction at ambient pressure and compared the thermally induced phase transition with the above-mentioned metastable CuNbO3. The present thermal decomposition reaction is a topochemical reaction with the elimination of cations, which has been little reported thus far.
|