eibunmei

2019 Fiscal Year Final Research Report

• Project/Area Number: 17H02724
• Research Category: Grant-in-Aid for Scientific Research (B)
• Allocation Type: Single-year Grants
• Section: 一般
• Research Field: Nanostructural chemistry
• Research Institution: Kyoto University
• Principal Investigator: Sakaguchi Hiroshi 京都大学, エネルギー理工学研究所, 教授 (30211931)
• Project Period (FY): 2017-04-01 – 2020-03-31
• Keywords: ナノ材料

Outline of Final Research Achievements

Two-dimensional graphene nanoribbons networks were fabricated from organic synthesized Z-bar linkage precursor molecules using our developed two-zone chemical vapor deposition technique. Two-dimensional graphene nanoribbons networks consist of fused wider GNR structures and ladder type structure via a C-C bond formation of adjacent GNRs. Upon a transition from the one-dimensional GNRs to two-dimensional graphene nanoribbons networks by an annealing, the electrical conductivities and carrier mobilities enhanced more than 5 orders magnitude. Additionally, 2D structures showed the significantly small thermal conductivities regarded as one of the most lowest values from carbon based materials.

Free Research Field

ナノ科学

Academic Significance and Societal Importance of the Research Achievements

本研究で明らかにした、二次元GNRネットワークはある程度の大きさの電気電導性と非常に低い熱伝導率を有しており、熱電材料としての有用性が示されたと考えられる。GNR鎖同士の脱水素縮環反応を利用した従来に無い広い幅を持つGNR構造や炭素―炭素単結合により形成した梯子型二次元炭素構造は、本研究で見出された新しい二次元ナノ炭素構造である。また、二次元ナノ炭素構造は、ある程度大きな電気伝導性と低い熱伝導性を持つことが示され、ボトムアップ合成GNRの熱電材料としての有用性を初めて示した研究と位置づけられる。これらの成果は、表面ボトムアップ合成GNRのエネルギー利用の可能性を示した研究である。