2019 Fiscal Year Final Research Report
Development of organometallic molecular ion beam deposition method for the stoichiometric crystal growth
Project/Area Number |
17H02997
|
Research Category |
Grant-in-Aid for Scientific Research (B)
|
Allocation Type | Single-year Grants |
Section | 一般 |
Research Field |
Plasma science
|
Research Institution | Osaka University |
Principal Investigator |
|
Co-Investigator(Kenkyū-buntansha) |
竹内 孝江 奈良女子大学, 自然科学系, 准教授 (80201606)
|
Project Period (FY) |
2017-04-01 – 2020-03-31
|
Keywords | 有機金属 / イオンビーム / 結晶成長 |
Outline of Final Research Achievements |
Fragment ions produced from hexamethyldisilane, tetraethylorthosilicate, or hexamethyldigermane in a Freeman-type ion source were investigated using a low-energy mass-selected ion beam system. Among these fragment ions, SiCH3+, Si(OH)3+, or GeCHx+ ions were mass-selected. The ion energy was in the range of 10-200 eV. Then, the SiCH3+, Si(OH)3+, or GeCHx+ ions were irradiated to Si substrates and resulting deposited films were analyzed. Following the completion of the ion irradiation experiment, X-ray photoelectron spectroscopy and Fourier-transform infrared spectroscopy assays of the films demonstrated the occurrence of silicon carbide, silicon dioxide, or germanium carbide depositions. We conclude that the irradiation of the mass-selected fragment ions, obtained from hexamethyldisilane, tetraethylorthosilicate, or hexamethyldigermane to substrates is useful for the secure growth of silicon carbide, silicon dioxide, or germanium carbide films.
|
Free Research Field |
量子ビーム科学関連
|
Academic Significance and Societal Importance of the Research Achievements |
(1)本研究では、有機金属ナノクラスターイオンビーム法を開発し、これによるストイキオメトリ結晶形成技術の基盤を確立した。(2)本研究で成膜に成功した結晶種は、例えば、シリコンカーバイド(SiC)である。SiCは次世代の省エネ大電力用ワイドギャップ半導体である。(3)SiC成膜に通常用いられるシランは自己発火性がある。一方、本研究で原料に用いたヘキサメチルジシランは危険性が低く、これを使えば安全に成膜を行うことができる。(4)本研究で用いた原料はいずれもたいへん安価である。本研究の技術を使用すれば、SiCなどの半導体膜や酸化ケイ素などの絶縁体膜を、社会に安価で供給できるようになる。
|