2011 Fiscal Year Final Research Report
Development of a micron-scale plasticity theory and its engineering application
| Project/Area Number |
21560076
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Materials/Mechanics of materials
|
|---|
| Research Institution | Yamagata University |
|---|
Principal Investigator |
|
|---|
| Project Period (FY) |
2009 – 2011
|
| Keywords | 連続体力学 / 結晶塑性 / 連続分布転位論 / 格子欠陥 |
|---|
| Research Abstract |
Mechanical behavior of metals at the micron scale were systematically investigated, and a physically-based gradient crystal plasticity theory has been formulated. In the experimental part of the study, microbend tests with reversal of bending direction were carried out on aluminium and copper single-crystal foils. The results strongly suggested that internal stresses, which act as back-stresses, existed in the bent foil specimens due to a non-uniform array of the geometrically necessary dislocations (GNDs). In the theoretical part, the effect of the GNDs was incorporated into a framework of gradient crystal plasticity theory.
|
Research Products
(11 results)