| Project/Area Number |
17360005
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (B)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Applied materials science/Crystal engineering
|
|---|
| Research Institution | Saitama University |
|---|
Principal Investigator |
SAKAI Masamichi Saitama University, 大学院・理工学研究科, 准教授 (40192588)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
田島 裕之 東京大学, 物性研究所, 准教授 (60207032)
|
|---|
| Co-Investigator(Renkei-kenkyūsha) |
田島 裕之 東京大学, 物性研究所, 准教授 (60207032)
|
|---|
| Research Collaborator |
中村 修 , カシオ計算機(株)
|
|---|
| Project Period (FY) |
2005 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥13,750,000 (Direct Cost: ¥13,300,000、Indirect Cost: ¥450,000)
Fiscal Year 2008: ¥1,040,000 (Direct Cost: ¥800,000、Indirect Cost: ¥240,000)
Fiscal Year 2007: ¥910,000 (Direct Cost: ¥700,000、Indirect Cost: ¥210,000)
Fiscal Year 2006: ¥3,100,000 (Direct Cost: ¥3,100,000)
Fiscal Year 2005: ¥8,700,000 (Direct Cost: ¥8,700,000)
|
|---|
| Keywords | 水素 / 希土類元素 / 輸送係数 / ホール係数 / 比抵抗 / 両極性伝導 / 誘電関数 / YHx / ホール抵抗 / フェルミ面 / バンド構造 / キャリヤ散乱機構 / 反射スペクトル / サマリウムニ水素化物 / プラズマ周波数 / イットリウムニ水素化物 / 磁気力 / 横磁気抵抗 / モリブデン / イットリウム二水素化物 / 補償金属 / 反射スペルトル / ドルーデ型誘電関数 / イットリウム |
|---|
| Research Abstract |
水素吸蔵能力の最も高い元素のひとつであるイットリウム(Y)に注目し, Y格子中への水素浸入の仕方が格子定数, 誘電関数, 電気抵抗率, ホール係数に及ぼす影響を調査した. 定比組成(YH_2)からの水素濃度変位は, i) 格子定数を殆ど変化させないが, 誘電関数すなわち電子構造に影響すること, ii) 残留抵抗の変動を通じてホール係数の変動を誘起すること, iii) このとき, 残留抵抗とホール係数との間に線形な相関が成立することが分かった. この相関の原因として, 正孔濃度≒電子濃度, 正孔移動度≒電子移動度という特性もつ両極性伝導機構を提案し, このモデルと磁気抵抗測定によって, YH_x(x≒2)のキャリヤの濃度と移動度を評価した.
|