STUDY ON FATIGUE DAMAGE ACCUMULATION UNDER VARIABLE AMPLITUDE LOADING IN ULTRA-HIGH CYCLE REGIME
| Project/Area Number |
18560089
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Materials/Mechanics of materials
|
|---|
| Research Institution | Fukui University of Technology |
|---|
Principal Investigator |
JONO Masahiro Fukui University of Technology, 工学部, 教授 (20029094)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
HAGI Hideki 福井工業大学, 工学部, 教授 (40117213)
SUGETA Atsushi 広島大学, 大学院工学研究科, 教授 (60162913)
|
|---|
| Project Period (FY) |
2006 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥3,980,000 (Direct Cost: ¥3,500,000、Indirect Cost: ¥480,000)
Fiscal Year 2008: ¥1,040,000 (Direct Cost: ¥800,000、Indirect Cost: ¥240,000)
Fiscal Year 2007: ¥1,040,000 (Direct Cost: ¥800,000、Indirect Cost: ¥240,000)
Fiscal Year 2006: ¥1,900,000 (Direct Cost: ¥1,900,000)
|
|---|
| Keywords | 疲労 / 変動荷重 / 超長寿命 / 高硬度鋼 / 2重S-N曲線 / 内部疲労き裂 / 疲労き裂進展 / 機械材料・機械力学 / 超長寿命域 / 機械材料・材料力学 |
|---|
| Research Abstract |
107サイクルを超える超長寿命域にわたる長時間の自動荷重変動疲労試験を可能とするとともに、高硬度材の2段変動荷重回転曲げ試験を実施し、高応力が先に負荷される場合や応力が頻繁に変動する場合には、超長寿命域疲労においても荷重変動の影響が現れ、寿命が短くなることを示した。また、軸荷重試験による内部き裂起点型破壊では、変動荷重下のfish-eye 内のき裂進展速度は、線形則により推定できることを明らかにした。
|
Report
(4 results)
Research Products
(18 results)