| Project/Area Number |
18K19131
|
|---|
| Research Category |
Grant-in-Aid for Challenging Research (Exploratory)
|
| Allocation Type | Multi-year Fund |
|---|
| Review Section |
Medium-sized Section 36:Inorganic materials chemistry, energy-related chemistry, and related fields
|
|---|
| Research Institution | Kobe University |
|---|
Principal Investigator |
Matsui Masaki 神戸大学, 工学研究科, 准教授 (70639210)
|
|---|
| Project Period (FY) |
2018-06-29 – 2020-03-31
|
| Project Status |
Completed (Fiscal Year 2019)
|
| Budget Amount *help |
¥6,370,000 (Direct Cost: ¥4,900,000、Indirect Cost: ¥1,470,000)
Fiscal Year 2019: ¥1,950,000 (Direct Cost: ¥1,500,000、Indirect Cost: ¥450,000)
Fiscal Year 2018: ¥4,420,000 (Direct Cost: ¥3,400,000、Indirect Cost: ¥1,020,000)
|
|---|
| Keywords | インサーション材料 / アコイオン / 蓄電池 / 正極活物質 / インサーション / 多価イオン |
|---|
| Outline of Final Research Achievements |
We investigate the electrochemical performances of olivine-FePO4, V2O5 nano-sheet and Mo3S4 in a magnesium-based aqueous system. The olivine-FePO4 and V2O5 nano-sheet showed reversible electrochemical activity, while Mo3S4 shows continuous H+ reduction. The catalytic activity of Mo as hydrogen reduction process may cause the electrochemical inactivity of Mo3S4.
|
| Academic Significance and Societal Importance of the Research Achievements |
先行研究においては，オリビン型FePO4中におけるマグネシウムイオンの固相内拡散は活性化障壁が高すぎるために困難と言われてきた．本検討で，多価イオンのインサーション反応が，電解液中の水分子によって影響を受けることが確認された．特に，水和水の共挿入が起こらないと考えられるFePO4の場合にも可逆性が著しく向上したという点は，活物質の最表面における反応性が，バルクの反応にも大きく影響することを示唆するものであり，インサーション材料の新たな設計指針を示すものであると言える．
|