Supramolecular self-supporting membrane having chiral nano-channel from supramolecular ladder chiral double helical polymer
| Project/Area Number |
19350054
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (B)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Polymer chemistry
|
|---|
| Research Institution | Niigata University |
|---|
Principal Investigator |
AOKI Toshiki Niigata University, 自然科学系, 教授 (80212372)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
KANEKO Takashi 新潟大学, 超域研究機構, 教授 (90272856)
TERAGUCHI Masahiro 新潟大学, 自然科学系, 助教 (30334650)
NAMIKOSHI Takeshi 新潟大学, ベンチャー・ビジネス・ラボラトリー, VBL研究機関研究員 (30452072)
HADANO Shingo 京都大学, 工学研究科, 産学官連携研究員 (70397157)
|
|---|
| Project Period (FY) |
2007 – 2009
|
| Project Status |
Completed (Fiscal Year 2009)
|
| Budget Amount *help |
¥17,290,000 (Direct Cost: ¥13,300,000、Indirect Cost: ¥3,990,000)
Fiscal Year 2009: ¥3,900,000 (Direct Cost: ¥3,000,000、Indirect Cost: ¥900,000)
Fiscal Year 2008: ¥3,770,000 (Direct Cost: ¥2,900,000、Indirect Cost: ¥870,000)
Fiscal Year 2007: ¥9,620,000 (Direct Cost: ¥7,400,000、Indirect Cost: ¥2,220,000)
|
|---|
| Keywords | らせん選択重合 / ラダー高分子 / キラルらせん高分子 / 膜 / 高分子反応 / 分解反応 / 自立膜 / 超分子膜 |
|---|
| Research Abstract |
独創的な構造を持つ「超分子ラダーキラル二重らせん高分子」を申請者らの見出した手法で数種類合成することに成功した。この高分子のみよりなる自立膜が、光により定量的な選択芳香族環化分解を行い、しかも自立膜性を保つことを見出した。これにより『超分子ポリマー膜』の新しい調製法、超高分子量ポリマーのミクロ構造分析法、キラルナノチャンネル超分子ポリマー自立膜の調製法を見出した。
|
Report
(4 results)
Research Products
(26 results)