Toughness enhancement of ultra-fine grained W-TiC for fusion divertor applications
| Project/Area Number |
19360412
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (B)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Nuclear fusion studies
|
|---|
| Research Institution | Tohoku University |
|---|
Principal Investigator |
KURISHITA Hiroaki Tohoku University, 金属材料研究所, 准教授 (50112298)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
NAKAI Kiyomichi 愛媛大学, 理工学研究科, 教授 (60038114)
KOBAYASHI Sengo 愛媛大学, 理工学研究科, 准教授 (10304651)
SAKAMOTO Tatsuaki 愛媛大学, 理工学研究科, 助教 (80403848)
HATAKEYAMA Masahiko 東北大学, 金属材料研究所, 助教 (30375109)
|
|---|
| Project Period (FY) |
2007 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥20,150,000 (Direct Cost: ¥15,500,000、Indirect Cost: ¥4,650,000)
Fiscal Year 2008: ¥7,670,000 (Direct Cost: ¥5,900,000、Indirect Cost: ¥1,770,000)
Fiscal Year 2007: ¥12,480,000 (Direct Cost: ¥9,600,000、Indirect Cost: ¥2,880,000)
|
|---|
| Keywords | タングステン / 炭化チタン / 再結晶・粒成長組織 / 結晶粒界 / 塑性加工 / 超塑性 / 室温延性 / 微細結晶粒 / 再結晶.粒成長組織 / 靭性 / 超微細粒 |
|---|
| Research Abstract |
先に研究代表者等により開発された超微細粒W-TiCは、耐照射特性に優れる等の多くの利点をもつが、厳しい熱負荷に晒される国際熱核融合実験炉(ITER)のダイバータに用いるためには高靱性化が必要である。高靱性化には塑性加工が有効であるので、超微細粒W-TiCの超塑性発現を塑性加工に適用する。まず、高温引張試験により超微細粒W-TiCの超塑性挙動を明らかにし、次にその結果を活用して塑性加工法を発案、実施した結果、再結晶・粒成長組織を示すにも関わらず結晶粒界が極めて強く、室温で曲げ延性を示す高靭性W-TiCの試作に成功した。
|
Report
(3 results)
Research Products
(27 results)
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
[Presentation] Development of Ultra-fine Grained W-TiC with Improved Toughness and Radiation Performance2008
Author(s)
H.Kurishita, H.Arakawa, S.Matsuo, T.Sakamoto, S.Kobayashi, K.Nakai, T.Takida, M.Kato, T.Yamamoto, K.Takebe, M.Kawai, N.Yoshida
Organizer
9th Inter.Workshop on Spallation Materials Technologies
Place of Presentation
Sapporo, Japan
Related Report
-
-
-
-
-
-
-
-
-
-
-