| Project/Area Number |
19560755
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Properties in chemical engineering process/Transfer operation/Unit operation
|
|---|
| Research Institution | Hiroshima University |
|---|
Principal Investigator |
YOSHIOKA Tomohisa Hiroshima University, 大学院・工学研究科, 准教授 (50284162)
|
|---|
| Co-Investigator(Renkei-kenkyūsha) |
TSURU Toshinori 広島大学, 大学院・工学研究科, 教授 (20201642)
|
|---|
| Project Period (FY) |
2007 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥4,420,000 (Direct Cost: ¥3,400,000、Indirect Cost: ¥1,020,000)
Fiscal Year 2008: ¥1,950,000 (Direct Cost: ¥1,500,000、Indirect Cost: ¥450,000)
Fiscal Year 2007: ¥2,470,000 (Direct Cost: ¥1,900,000、Indirect Cost: ¥570,000)
|
|---|
| Keywords | 多孔性セラミック膜 / 気体分離 / 分子動力学法 / 金属ドープ |
|---|
| Research Abstract |
多孔性セラミック気体分離膜材料として, 金属添加シリカおよびジルコニアコロイドゾルを調製し, ゲル粉体試料の構造を評価した. これらのセラミック材料を用いることにより, 高透過選択性と安定性を有する多孔性セラミック水素分離膜の作製が可能であった. また, 様々な構造を有するアモルファスシリカ膜における気体透過現象を分子動力学シミュレーションにより再現し, 気体透過特性とアモルファス多孔性セラミック膜構造の関係を明らかとした.
|