Research and development of a functional material with low adsorption and solubility of tritium for fusion systems.
| Project/Area Number |
19560826
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Nuclear fusion studies
|
|---|
| Research Institution | University of Toyama |
|---|
Principal Investigator |
MATSUYAMA Masao University of Toyama, 水素同位体科学研究センター, 教授 (90135004)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
TORIKAI Yuji 富山大学, 水素同位体科学研究センター, 准教授 (80313592)
|
|---|
| Project Period (FY) |
2007 – 2009
|
| Project Status |
Completed (Fiscal Year 2009)
|
| Budget Amount *help |
¥4,290,000 (Direct Cost: ¥3,300,000、Indirect Cost: ¥990,000)
Fiscal Year 2009: ¥1,040,000 (Direct Cost: ¥800,000、Indirect Cost: ¥240,000)
Fiscal Year 2008: ¥1,430,000 (Direct Cost: ¥1,100,000、Indirect Cost: ¥330,000)
Fiscal Year 2007: ¥1,820,000 (Direct Cost: ¥1,400,000、Indirect Cost: ¥420,000)
|
|---|
| Keywords | 高濃度トリチウム / メモリー効果 / 吸着量 / 溶解度 / 銅基合金 / 核融合炉材料 / トリチウム / 溶解量 / Cu-Be合金 |
|---|
| Research Abstract |
トリチウムガスに曝されても吸着・吸収による汚染が起こり難い材料の探索を目途として、銅基合金材料表面への吸着及び内部への溶解挙動を調べた。表面層にトリチウム高濃度領域が存在したが、内部は表面層に比べ1/1000以下の濃度であり、ステンレス鋼に対する溶解度の約1/300であった。この際の溶解熱は17kJ/molとなり、純Cuに対する報告値の約1/3に低下した。即ち、本合金が有望な候補材になり得る事が知られた。
|