Basic Section 27030:Catalyst and resource chemical process-related
|
|---|
| Research Institution | National Institute of Advanced Industrial Science and Technology |
|---|
Principal Investigator |
Norihito Hiyoshi 国立研究開発法人産業技術総合研究所, 材料・化学領域, 研究グループ長 (50415733)
|
|---|
| Project Period (FY) |
2020-04-01 – 2023-03-31
|
| Project Status |
Completed (Fiscal Year 2022)
|
| Budget Amount *help |
¥4,290,000 (Direct Cost: ¥3,300,000、Indirect Cost: ¥990,000)
Fiscal Year 2022: ¥1,040,000 (Direct Cost: ¥800,000、Indirect Cost: ¥240,000)
Fiscal Year 2021: ¥1,560,000 (Direct Cost: ¥1,200,000、Indirect Cost: ¥360,000)
Fiscal Year 2020: ¥1,690,000 (Direct Cost: ¥1,300,000、Indirect Cost: ¥390,000)
|
|---|
| Keywords | ヘテロポリ酸 / 電子顕微鏡 / 触媒膜 |
|---|
| Outline of Research at the Start |
本研究では、触媒活性を有するケギン型ヘテロポリ酸分子を薄膜状に集積させた多孔質膜を開発し、それを用いた触媒膜反応システムの構築を目指す。多孔質膜を作成するために、気液界面における二次元的な結晶成長や、層状ヘテロポリ酸塩の層剥離と再構築などの手法を開発する。また、多孔質膜の構造および生成過程を主に収差補正電子顕微鏡を用いて明らかにし、その知見を基に多孔質膜の作成手法を最適化する。さらに、得られた多孔質膜の触媒特性を明らかにする。
|
| Outline of Final Research Achievements |
In this study, we investigated methods for assembling heteropolyacid molecules in order to fabricate Keggin-type heteropolyacid membranes with catalytic activity. It was clarified that a film can be formed by adding an alkylamine to an aqueous solution containing Keggin-type heteropolyacid and alkali metal salt. Furthermore, by improving the observation conditions of scanning transmission electron microscopy, we succeeded in atomic resolution observation of aggregates of heteropolyacid molecules.
|
| Academic Significance and Societal Importance of the Research Achievements |
本研究ではへテロポリ酸分子を二次元的に集積するための条件を明らかにし、新規な集積体を開発した。この成果は、新規な固体ヘテロポリ酸触媒の開発につながると期待できる。また、本研究では、走査透過電子顕微鏡の観察条件を検討したことにより、電子に弱いヘテロポリ酸集積体の原子レベルでの構造評価を可能とした。これにより、ヘテロポリ酸触媒のより詳細な構造解明に繋がると期待できる。
|