Investigation of caries treatment by hyper-effective remineralization on nano-level

2018 Fiscal Year Final Research Report

• Project/Area Number: 15K11101
• Research Category: Grant-in-Aid for Scientific Research (C)
• Allocation Type: Multi-year Fund
• Section: 一般
• Research Field: Conservative dentistry
• Research Institution: Asahi University
• Principal Investigator: OKUYAMA Katsushi 朝日大学, 歯学部, 准教授 (00322818)
• Co-Investigator(Kenkyū-buntansha): 玉置 幸道 朝日大学, 歯学部, 教授 (80197566) ; 松田 康裕 北海道医療大学, 歯学部, 講師 (50431317) ; 星加 修平 北海道大学, 歯学研究院, 助教 (40581682)
• Research Collaborator: YAMAMOTO hiroko
• Project Period (FY): 2015-04-01 – 2019-03-31
• Keywords: 再石灰化 / フッ素 / ハイドロキシアパタイト / PIXE/PIGE法 / 水酸化カリウム不溶性フッ素 / フルオロアパタイト

Outline of Final Research Achievements

The effects of topical fluoride applications and fluoride-containing dental materials were evaluated on the conversion from hydroxyapatite (HAP) to fluorapatite (FAP). The results of this study show that the amount of FAP or ratio of FAP/HAP after topical fluoride application was depended on concentration, or pH of solution, or duration application periods. The use of higher fluoride release materials indicated higher fluoride uptake to tooth and conversion of FAP. Fluoride varnish with hydrogen gel showed high fluoride uptake and low demineralization on adjacent tooth with materials. The details of the conversion from HAP to FAP, and the usefulness of hydrophilic gel containing into fluoride varnish for caries prevention were suggested in this research.

Free Research Field

歯科保存学、材料学

Academic Significance and Societal Importance of the Research Achievements

フッ化物適用によりハイドロキシアパタイトがフルオロアパタイトに置換し、耐酸性が向上することで抗う蝕性を示すことは知られているが、フッ化物の使用量や期間などによる影響はあまり知られていない。適切な条件を提示することで、効率的な再石灰化をはじめとするう蝕予防につながる。また、親水性ゲルの使用は長期にわたるフッ素供給として有用なことを示しており、根面う蝕などの予防に役立つものと思われる。