2018 Fiscal Year Final Research Report
Fabrication of beta-tricalcium phosphate cement and their tissue responses
Project/Area Number |
16K11649
|
Research Category |
Grant-in-Aid for Scientific Research (C)
|
Allocation Type | Multi-year Fund |
Section | 一般 |
Research Field |
Dental engineering/Regenerative dentistry
|
Research Institution | Kyushu University |
Principal Investigator |
Munar Melvin 九州大学, 歯学研究院, 学術研究員 (50432919)
|
Co-Investigator(Kenkyū-buntansha) |
石川 邦夫 九州大学, 歯学研究院, 教授 (90202952)
|
Research Collaborator |
Tsuru Kanji
|
Project Period (FY) |
2016-04-01 – 2019-03-31
|
Keywords | 顆粒セメント / 骨補填材 / β-TCP |
Outline of Final Research Achievements |
Calcium sulfate dihydrate (CSD)-coated β-tricalcium phosphate (TCP) granules were produced by immersing β-tricalcium phosphate in NaHSO4 solution. The CSD-coated β-TCP granules were heated, resulting in the formation of calcium sulfate hemihydrate (CSH)-coated β-TCP granules. When the CSH-coated β-TCP granules were mixed with saline, they set to be cement composed of β-TCP granules. The CSH-coated β-TCP granules were implanted into the defect of rabbit femur. The CSH-coated β-TCP granules set in the defect. At four weeks after implantation, 28% of new bone was formed.
|
Free Research Field |
生体材料
|
Academic Significance and Societal Importance of the Research Achievements |
本研究で作製したCSH被覆β-TCP顆粒は、中性で自己硬化性を示す顆粒セメントである。このセメントは、顆粒から成るため、骨欠損部において多孔体が形成されるという特徴がある。これは粉末から成るセメントにはない特徴であり、セメント内への細胞やタンパク等の侵入を容易にする。この顆粒セメントは、母床骨と顆粒、顆粒同士の連続性が確保されている。また、顆粒をそのまま埋入する場合に比べて高い骨形成能が得られることを確認している。以上より、この顆粒セメントは、歯科や整形外科領域において有用であると思われる。
|