Basic study of smart dental cement - for both strong bonding and easy debonding

2018 Fiscal Year Final Research Report

• Project/Area Number: 16K15804
• Research Category: Grant-in-Aid for Challenging Exploratory Research
• Allocation Type: Multi-year Fund
• Research Field: Prosthodontics/ Dental materials science and
• Research Institution: The University of Tokushima
• Principal Investigator: HAMADA Kenichi 徳島大学, 大学院医歯薬学研究部(歯学域), 教授 (00301317)
• Research Collaborator: KAJIMOTO Noboru ; UYAMA Emi ; SEKINE Kazumitsu
• Project Period (FY): 2016-04-01 – 2019-03-31
• Keywords: 歯科用セメント / スマート材料 / 通電剥離 / イオン液体 / グラスアイオノマーセメント

Outline of Final Research Achievements

Recent advances in dental cement have made it possible to achieve strong bonding between dental restorations and tooth, but a large force is required when removing restorations, which may lead to tooth damage. In order to reduce this risk, smart dental cements that shows strong bonding strength but can reduce the strength on demand are required. In this study, we found that the addition of ionic liquid to the dental glass ionomer cement gives electrical conductivity, and while maintaining the bonding strength, the strength can be greatly reduced by applying current between the adherends.