simultaneous control of shape and microstructure to achieve the high-value-added manufacturing of magnesium alloy products

2020 Fiscal Year Final Research Report

• Project/Area Number: 18K14025
• Research Category: Grant-in-Aid for Early-Career Scientists
• Allocation Type: Multi-year Fund
• Review Section: Basic Section 26050:Material processing and microstructure control-related
• Research Institution: Ibaraki University
• Principal Investigator: Onuki Yusuke 茨城大学, フロンティア応用原子科学研究センター, 産学官連携助教 (50746998)
• Project Period (FY): 2018-04-01 – 2021-03-31
• Keywords: マグネシウム合金 / 集合組織 / 動的再結晶 / 曲げ加工

Outline of Final Research Achievements

Magnesium alloys are light and rigid structural materials while their ductility is not as good as steels and aluminum alloys. In this study, however, we observed an excellent ductility of Ca-added magnesium alloy at high temperatures (200～300℃). By heating only the part to be deformed, a large deformation could be achieved, which consumed minimum energy.

Free Research Field

金属組織学

Academic Significance and Societal Importance of the Research Achievements

軽量高強度のマグネシウム合金の利用拡大は、自動車・鉄道車両などの軽量化に寄与し、二酸化炭素排出量の低下に貢献できる。本研究はマグネシウム合金の「形を作る」プロセスを提案することで、この社会的課題に対するアプローチを示しました。学術的な観点からは、高温でのマグネシウム合金の延性改善メカニズムが、鉄鋼やアルミニウム合金とは異なる現象に起因していることを明らかにした。これについてはまだ不明な点が多いですが、今後の研究によって、「延性に乏しくすぐ割れる」というマグネシウム合金の常識を覆す可能性がある。