Improvement in performance of electroplated magnetic films using halogen ions and improvement principle

2021 Fiscal Year Final Research Report

• Project/Area Number: 19K04472
• Research Category: Grant-in-Aid for Scientific Research (C)
• Allocation Type: Multi-year Fund
• Section: 一般
• Review Section: Basic Section 21050:Electric and electronic materials-related
• Research Institution: Nagasaki University
• Principal Investigator: Yanai Takeshi 長崎大学, 工学研究科, 准教授 (30404239)
• Project Period (FY): 2019-04-01 – 2022-03-31
• Keywords: 軟磁性 / 硬磁性 / 厚膜 / 電解めっき / 深共晶溶媒

Outline of Final Research Achievements

The purpose of this project was to improve the magnetic properties of hard and soft magnetic films such as Fe-Pt, Fe-Ni, and Fe-Co alloys. For the soft magnetic Fe-Ni and Fe-Co films, the presence of halogen ions in the plating bath improved the soft magnetic properties slightly. On the other hand, for the hard magnetic Fe-Pt films, we found that the halogen ions reduce the coercivity and that the addition of alkali metal ions in the bath suppresses the reduction in the coercivity by the alkali metal ions.

Free Research Field

電子・電気材料工学

Academic Significance and Societal Importance of the Research Achievements

軟磁性膜においてはその高性能化により，より高い周波数での駆動が期待できる。これにより，磁気デバイスの小型・省エネ化が期待でき，電気自動車をはじめとする様々なモノの電化への貢献が期待できる。硬磁性膜においては，ハロゲンイオンが磁気特性の劣化要因になることを見出したことから，ハロゲンイオンフリーのめっき浴開発が進むと予想され，特性の優れた硬磁性材料開発をサポートする知見が得られたことなどが，本研究成果の意義である。