2021 Fiscal Year Final Research Report
Development of evaluation method for member strength of FRP members with fiber nonuniformity in cross section
| Project/Area Number |
19K04578
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Multi-year Fund |
|---|
| Section | 一般 |
|---|
| Review Section |
Basic Section 22020:Structure engineering and earthquake engineering-related
|
|---|
| Research Institution | Kobe University |
|---|
Principal Investigator |
|
|---|
| Project Period (FY) |
2019-04-01 – 2022-03-31
|
| Keywords | ガラス繊維強化プラスチック / 部材強度 / 繊維含有率 / 引張強度 / 圧縮強度 / せん断強度 |
|---|
| Outline of Final Research Achievements |
The purpose of this study is to develop a strength evaluation method for reinforced fiber plastic members that takes into account the effect of variations in fiber content in the cross section of the member. Loading tests were conducted on channel members made of glass fiber-reinforced plastic (GFRP). In this experiment, two types of GFRP and two sizes of channel members were used to conduct tensile, compression, and shear tests on coupon specimens, plate element specimens, and member specimens. The results revealed the ratio of member strength to the average strength of the coupon and plate element tests in tensile and compressive strength. In the shear tests, it was found that the member strength could not be predicted solely from the coupon tests because the failure modes differed depending on the member dimensions.
|
| Free Research Field |
鋼構造，複合構造
|
| Academic Significance and Societal Importance of the Research Achievements |
現在，土木分野では，構造物の劣化が顕著となっており社会問題化している．その中で，高耐久性のある構造材料の開発が進められており，その一つとして，本研究では繊維強化プラスチック材料を用いた構造部材に着目し，その部材強度の評価方法を検討した．本研究成果により，より精度の高い部材強度評価が行うことができ，このような構造部材の適用性が高まることで，より耐久性が高い構造物の開発につながると考えられる．
|