Production of a casting anisotropic neodymium magnet via electromagnetic vibration processing

2021 Fiscal Year Final Research Report

• Project/Area Number: 19K05071
• Research Category: Grant-in-Aid for Scientific Research (C)
• Allocation Type: Multi-year Fund
• Section: 一般
• Review Section: Basic Section 26040:Structural materials and functional materials-related
• Research Institution: National Institute of Advanced Industrial Science and Technology
• Principal Investigator: TAMURA Takuya 国立研究開発法人産業技術総合研究所, 材料・化学領域, 研究チーム長 (30446588)
• Co-Investigator(Kenkyū-buntansha): 李 明軍 国立研究開発法人産業技術総合研究所, 材料・化学領域, 主任研究員 (50392808)
• Project Period (FY): 2019-04-01 – 2022-03-31
• Keywords: ネオジム磁石 / 電磁振動 / 異方性 / 結晶配向 / 鋳造磁石

Outline of Final Research Achievements

For the "NdCu + Nd2Fe14B" alloy, we experimented to clarify the mechanism of uniform fine dispersion and c-axis orientation of the solid Nd2Fe14B magnet phase in the liquid NdCu non-magnetic phase by the electromagnetic vibration process. As a result, it is possible to obtain characteristics of residual magnetization: 0.8T and coercive force: 1.0T without using heavy rare earth metals, and it was possible to realize the same characteristics as commercially available anisotropic neodymium bond magnets.

Free Research Field

金属における凝固プロセス

Academic Significance and Societal Importance of the Research Achievements

本研究において見出した鋳造のみによる異方性ネオジム磁石の作製は世界初であり、さらに均一微細分散化かつc軸配向するメカニズムを明らかすることで、様々な値を定量化する事ができ、特に固相のネオジム磁石相は非常に小さいエネルギーにて破砕する事が出来る事を見出した。このことは、今後様々なセミソリッドプロセスによる異方性磁石作製がが可能になる可能性を指し示すものである。