Exploratory research of innovative pulp capping materials both with promoting healing of dental pulp and adhesive property to hard tissue

2021 Fiscal Year Final Research Report

• Project/Area Number: 19K10123
• Research Category: Grant-in-Aid for Scientific Research (C)
• Allocation Type: Multi-year Fund
• Section: 一般
• Review Section: Basic Section 57030:Conservative dentistry-related
• Research Institution: Hokkaido University
• Principal Investigator: sano hidehiko 北海道大学, 歯学研究院, 教授 (90205998)
• Co-Investigator(Kenkyū-buntansha): 松本 真理子 北海道大学, 大学病院, 助教 (30733969) ; 樋田 京子 北海道大学, 歯学研究院, 教授 (40399952)
• Project Period (FY): 2019-04-01 – 2022-03-31
• Keywords: 歯髄 / 接着歯学 / 直接覆髄 / 高分子材料 / 生体材料 / 歯科理工学 / 直接覆髄材 / MTAセメント

Outline of Final Research Achievements

Based on the study by Toida et al, (Dent Mater J. ;41:126-133 2022), the combination of MTA and phosphorylated-pullulan resulted in good healing of exposed monkey pulp. Moreover, adhesive property of phosphorylated-pullulan made it possible to user friendly handlings and perfect dentin sealing. A report of pupal reactions after pulp capping treatments from Islam R et al, (Int Endod J. ;54:1902-1914 2021) stated interesting results. They used 4-META/MMA-TBB resin as a control material. The combination of MTA and phosphorylated-pullulan showed superior healing of pulp after application, compared to plain use of MTA. Additionally, plain use of phosphorylated-pullulan to the pulp did not show any adverse effect on the pulp healing. Preliminary study using colloidal platinum nanoparticles (CPN) to the exposed pulp demonstrated excellent pulp healing with less inflammatory reactions and prompt angiogenesis within the exposed pulp which might contribute to support good healing of the pulp.

Free Research Field

歯科保存学

Academic Significance and Societal Importance of the Research Achievements

MTAの有効性が新たなキャリア（リン酸化プルラン）を用いた場合にさらに発揮することが判明し，この成果をもとにクラス２の材料として認可されている．また，リン酸化プルランは、生体内で何ら悪影響を及ぼさないことが判明し，将来的に生体内硬組織への接着性キャリアとして応用可能であろうことが示唆された．白金ナノコロイド（CPN）は，生体内に作用させると，ほとんど炎症が認められないことや短期間で血管造成が見られることから，抗炎症作用と治癒促進作用を有すると考えられる．これに関する将来の検討が，新たな生体への機能的材料開発の糸口となる可能性を秘めている