Production of toxic element-free Ca cement for regenerating hard tissue

2022 Fiscal Year Final Research Report

• Project/Area Number: 19K10194
• Research Category: Grant-in-Aid for Scientific Research (C)
• Allocation Type: Multi-year Fund
• Section: 一般
• Review Section: Basic Section 57040:Regenerative dentistry and dental engineering-related
• Research Institution: Asahi University
• Principal Investigator: Tamaki Yukimichi 朝日大学, 歯学部, 教授 (80197566)
• Co-Investigator(Kenkyū-buntansha): 奥山 克史 朝日大学, 歯学部, 准教授 (00322818) ; 新谷 耕平 朝日大学, 歯学部, 助教 (50824455) ; 川木 晴美 朝日大学, 歯学部, 教授 (70513670)
• Project Period (FY): 2019-04-01 – 2023-03-31
• Keywords: ケイ酸カルシウム / 覆髄材 / 珪藻土 / 生体親和性 / 電気炉焼成

Outline of Final Research Achievements

In recent years, calcium silicate cement represented by Mineral Trioxide Aggregate (MTA) and bioceramic materials made from bioglass have become popular as pulp capping materials. , calcium sulfate, dicalcium silicate, tricalcium silicate, etc., and is reported to exhibit excellent effects such as hard tissue induction and antibacterial effects due to the formation of calcium hydroxide accompanying the hydration reaction. Toxic substances contained in are also regarded as a problem.
In this study, dicalcium silicate and tricalcium silicate were synthesized and an attempt was made to create a new calcium silicate-based cement material.

Free Research Field

生体材料学

Academic Significance and Societal Importance of the Research Achievements

MTAセメントは歯科保存領域で、特に歯髄の保護、硬組織再生に有用な材料であることが報告されているが、一方では高価で使用に制限があることやポルトランドセメントに含まれるヒ素や鉛などの有害物質を問題視する意見もある。この有害物質を精錬し除去する工程のため、製品としてのMTAセメントが極めて高価になるとも言われている。本研究ではMTAセメントの効能がケイ酸二カルシウム、ケイ酸三カルシウムであるならば、ポルトランドセメントに頼らない、新たなケイ酸カルシウム系セメントを創製することを考えた。これにより広く歯科診療に提供が可能となり、多くの患者に福音となることが予想される。