Stabilization of parts quality using semi-sintering process in polymer laser sintering

2021 Fiscal Year Final Research Report

• Project/Area Number: 19K14867
• Research Category: Grant-in-Aid for Early-Career Scientists
• Allocation Type: Multi-year Fund
• Review Section: Basic Section 18020:Manufacturing and production engineering-related
• Research Institution: Tokyo Metropolitan Industrial Technology Research Institute
• Principal Investigator: Kobayashi Ryuichi 地方独立行政法人東京都立産業技術研究センター, 事業化支援本部技術開発支援部製品化技術グループ, 副主任研究員 (30707112)
• Project Period (FY): 2019-04-01 – 2022-03-31
• Keywords: 付加製造 / レーザ焼結 / パートケーキ / クラック / 半焼結 / オレンジピール

Outline of Final Research Achievements

We developed a semi-sintering process that can produce semi-sintered powder using low-power laser irradiation during building in order to control the location of cracks that propagate in unsintered powder of partcake in polymer laser sintering. The crack suppression rate was increased by using this process to semi-sinter powder between adjacent parts. Furthermore, applying the semi-sintering process to the sides of parts was effective in suppressing orange peel (unintended surface roughness), which is a problem inherent to polymer laser sintering.

Free Research Field

レーザ焼結

Academic Significance and Societal Importance of the Research Achievements

本研究で確立した半焼結プロセスによるオレンジピール抑制は、樹脂レーザ焼結の品質安定化に直結する。また、通常の装置運用において、リサイクル粉末（装置内で融点付近まで予熱された粉末）と新しい粉末を混合した粉末が装置に投入される。そして通説ではオレンジピール抑制のために新しい粉末を30-50%混合することが求められるが、半焼結プロセスによるオレンジピール抑制を適用することで、従来よりも新しい粉末の投入量を少なくできる可能性がある。したがって、半焼結プロセスの適用は低コスト、低環境負荷の樹脂レーザ焼結を実現できる可能性がある。