A development of implant surface modification preventing the adherence of peri-implantitis related bacteria

2020 Fiscal Year Final Research Report

• Project/Area Number: 19K19141
• Research Category: Grant-in-Aid for Early-Career Scientists
• Allocation Type: Multi-year Fund
• Review Section: Basic Section 57050:Prosthodontics-related
• Research Institution: Tokyo Dental College
• Principal Investigator: Oda Yukari 東京歯科大学, 歯学部, 助教 (20778518)
• Project Period (FY): 2019-04-01 – 2021-03-31
• Keywords: インプラント周囲炎 / streptococci / チタン / ジルコニア / 中性2%NaF

Outline of Final Research Achievements

As a result of collecting a sample at the site of peri-implantitis and performing a comprehensive analysis by metagenomic analysis, streptococci, which is considered to be an early colonizing bacteria in periodontitis, was detected. First, streptococci was evaluated for adhesion on titanium and zirconia. Streptococcal adhesion was less on zirconia than on titanium. Next, we focused on NaF, which is widely known for suppressing caries, and examined whether neutral 2% NaF is also effective in suppressing the adhesion of streptococci. In a group which 2% NaF was applied on titanium and zirconia, compared with the group without NaF application, the number of viable bacteria was smaller, suggesting that it may be effective in suppressing streptococcal adhesion.

Free Research Field

補綴系歯学

Academic Significance and Societal Importance of the Research Achievements

インプラント周囲炎はインプラント治療における生物学的合併症の一つであり、罹患患者は2018年時点で2割以上である。
しかし、明確な予防法および治療法がないために、医療保険適応項目であるインプラント除去となるケースが増加している。今回、チタンおよびジルコニア表面において、2%中性NaFが初期定着細菌streptococciの付着抑制に有効であることが明らかになった。本結果は、今後のインプラント周囲炎の予防法を確立するにあたり、基礎となるデータになるだろう。特にその臨床応用法を確立できれば、非常に有用であると考えられる。