Elucidation of the mechanism of extream pressure properties of oil-soluble polymers and the combination effect of polymers and other functional additives

2022 Fiscal Year Final Research Report

• Project/Area Number: 20K04254
• Research Category: Grant-in-Aid for Scientific Research (C)
• Allocation Type: Multi-year Fund
• Section: 一般
• Review Section: Basic Section 18040:Machine elements and tribology-related
• Research Institution: Tokyo Metropolitan Industrial Technology Research Institute
• Principal Investigator: Nakamura Kenta 地方独立行政法人東京都立産業技術研究センター, 研究開発本部機能化学材料技術部マテリアル技術グループ, 上席研究員 (20556849)
• Project Period (FY): 2020-04-01 – 2023-03-31
• Keywords: 油溶性ポリマー / 吸着 / AFM / 部分EHL / 境界潤滑 / SRV / MoDTC / ZnDTP

Outline of Final Research Achievements

It was known that polylaurylacrylatelacryrate (PLA/HEA) inhibited seizure in severe condition of boundary lubrication like an extreme pressure additive. From the results of comparing tribological properties both PLA/HEA and absorption type polymer, it was inferred that mechanism of inhibiting seizure with PLA/HEA was not adsorption, but reaction. Meanwhile, it was found that PLA/HEA did not obstruct tribological function of friction modifier or wear inhibitor.

Free Research Field

トライボロジー

Academic Significance and Societal Importance of the Research Achievements

油溶性添加剤における環境負荷低減の観点から、極圧剤・摩擦調整剤としての期待が高まるポリマーの、化学構造とトライボロジー特性の関係を明確にすることが求められている。本研究により、ポリマーの反応性と吸着性を類別した上で、化学構造と吸着性やトライボロジー特性を関連付けたこと、他の添加剤との併用効果を明らかにしたことは、環境適応型潤滑剤の開発における添加剤の設計指針を与えるものである。