tudy of the die-casting process used by high toughness aluminum alloy

2022 Fiscal Year Final Research Report

• Project/Area Number: 20K05129
• Research Category: Grant-in-Aid for Scientific Research (C)
• Allocation Type: Multi-year Fund
• Section: 一般
• Review Section: Basic Section 26040:Structural materials and functional materials-related
• Research Institution: University of Toyama
• Principal Investigator: Saikawa Seiji 富山大学, 学術研究部都市デザイン学系, 教授 (20642226)
• Project Period (FY): 2020-04-01 – 2023-03-31
• Keywords: ダイカスト / アルミニウム / 鋳造割れ / 軽量化 / Al-Mg-Si合金 / Sr添加 / 共晶微細化

Outline of Final Research Achievements

In the case of casting of Al-3～4%Mg-1～2%Mg system alloy used by die-castng machine over 350tons clamping force, we investigated the casting condition that hot-tearing decreased, and good quality parts obtained. As a result, when Sr addition in the alloy was about 0.02～0.06mass% and cooling rate was about 100-200℃/s at casting, hot-tearing decreased and good mechanical property in tensile test was obtained due to modify eutectic structure in the die-casting parts on an industrial scale.

Free Research Field

鋳造工学

Academic Significance and Societal Importance of the Research Achievements

Al-Mg-Si系合金へのSr添加による鋳造割れの抑止効果が，従来のラボスケールの小規模鋳造（概ね500g未満）のみならず，今回の研究により，初めて実工業レベルの大きな実部品形状（概ね1～2kg以上の機関系部品や箱型部品）においても有効であることを実証できた。このことは地球環境保全の一助である輸送車両の本系アルミニウム部材での軽量化が従来以上に適用できることをも意味しており，このことから本研究の成果は社会的意義を有すると言えよう。
一方で，金属組織中の共晶相がSr添加により微細化されることを，大きな実部品レベルで初めて冶金学的に明らかに出来た為，学術的意義もあったと判断される。