2010 Fiscal Year Final Research Report
Preparation of High Strength and Functional Nano Fiber from Mulberry Cellulose
| Project/Area Number |
21750216
|
|---|
| Research Category |
Grant-in-Aid for Young Scientists (B)
|
| Allocation Type | Single-year Grants |
|---|
| Research Field |
Polymer/Textile materials
|
|---|
| Research Institution | Shinshu University |
|---|
Principal Investigator |
TAKASAKI Midori Shinshu University, サテライト・ベンチャー・ビジネス・ラボラトリー, 助教 (00402149)
|
|---|
| Project Period (FY) |
2009 – 2010
|
| Keywords | ナノ材料 / 成形加工・処理 / バイオマス |
|---|
| Research Abstract |
1-Deoxynojirimycin (1-DNJ) content rate of ploidy breed was higher than common breed (ichinose) in mulberry leaves. In addition, inhibitory rate of sugar absorption for 1-DNJ sample extracted from leaves of mulberry which has improved in faculty of textile science and technology, Shinshu University was also higher than ichinose.
On mulberry/manila hemp cellulose filament, 30wt% of mulberry cellulose sample indicated the highest molecular orientation and mechanical properties. In comparison with webs of kouzo mulberry, that of ichinose mulberry cellulose had lower density and higher smoothness and air permeability. This result may suggest that nano fiber prepared from ichinose mulberry cellulose applies to high-functional material such as adsorption and wiping material.
|