Specific deformation behavior of crystalline polymer under biaxial deformation

2023 Fiscal Year Final Research Report

• Project/Area Number: 21H02003
• Research Category: Grant-in-Aid for Scientific Research (B)
• Allocation Type: Single-year Grants
• Section: 一般
• Review Section: Basic Section 35020:Polymer materials-related
• Research Institution: Kyushu University
• Principal Investigator: Kojio Ken 九州大学, 先導物質化学研究所, 准教授 (20346935)
• Project Period (FY): 2021-04-01 – 2024-03-31
• Keywords: Biaxial deformation / Crystalline polymer

Outline of Final Research Achievements

Since polymer chains have a one-dimensional structure, they show an anisotropic response to deformation. In this study, behaviors of molecular chains were investigated under the biaxial deformation process by wide-angle X-ray diffraction and polarized high-speed camera observation. Both measurements revealed that yielding in various directions occurred near the yield point.

Free Research Field

高分子科学

Academic Significance and Societal Importance of the Research Achievements

LLDPEやナイロンをはじめとする結晶性高分子材料は、一般に弾性率が高く剛性があり、単体のみならず、ガラス繊維、炭素繊維や種々のフィラーとの複合材料として使用されている。また、安価なものも多いため、高分子材料分野において、量的に非常に大きな割合を占めている。さらに、熱や溶媒を使用することによって、再成形なども可能であるため、持続可能な社会を達成する上で重要な役割を果たしうる。したがって、本研究で得られた成果は、このような結晶性高分子のさらなる用途開発に極めて重要な知見となると期待される。